Newton Waterproofing HydroCoat 103 2K Coating
HYDROCOAT 103 2K COATING
HYDROCOAT 103 2K COATING
High Performance Cementitious Coating
Rapid Defense, Lasting Protection : HydroCoat 103 2K ensures swift, airless application for unbeatable waterproofing. Withstand extreme pressures, safeguarding reservoirs, tanks, and structures for lasting protection.
INFORMATION
PRODUCT CODE
103-S
BRAND
Newton Waterproofing
PRODUCT TYPE
Waterproofing Material
PRODUCTION
Made in United Kingdom
MEMBRANE THICKNESS IN ONE OR TWO COATS
2.0 mm
WATER VAPOUR RESISTANCE – Μ VALUE
455 μ
COLOUR
Grey
ELONGATION
3 to 5%
PACKAGING
0kg (A+B Components, within two containers)
ADAPTABLE STRENGTH, ANYWHERE
Versatile HydroCoat 103 2K adapts to podiums, balconies, and more. Defends against sulphate challenges, forming a robust barrier with enhanced chemical resistance for enduring durability.
ADHESION TO CONCRETE
>2 MPa
WATER VAPOUR RESISTANCE
4.55 MNs/g
WATER VAPOUR RESISTANCE – SD VALUE
Value 0.91 m
SUITABLE SURFACES
-Soffit : Negative pressure
-Slab/raft : Negative pressure
-Decks & balconies : Positive pressure
-Walls : Positive pressure & negative pressure
COMPRESSIVE STRENGTH – 1 DAY
>10 MPa
COMPRESSIVE STRENGTH – 28 DAYS
>40 MPa
TYPICAL DATA
TOTAL DEFENSE, EXTENDED LIFESPAN
Beyond waterproofing, HydroCoat 103 2K fortifies against acids, moisture, and chlorides. Ideal for highways and coasts, it reinforces joints, promising comprehensive, long-lasting structural integrity.
MATERIAL
Steel & Concrete
PH
12-14
REACTION TO FIRE CLASSIFICATION
A2-s1
UV RESISTANCE – STABLE BUT WILL DISCOLOUR
50 Years
SUITABLE SUBSTRATES
Correctly prepared substrates of :
- Steel
- Concrete of at least 20 MPa
- Structural masonry/mortar
HARDNESS (28 DAYS)
>75 Shore D
TENSILE STRENGTH
>2.5 MPa
APPLICATION RATE
3.6kg/m² in one or two coats
TYPICAL WATERPROOFING APPLICATIONS
-Podium decks, balconies and car parking areas. -Concrete water-retaining structures such as water tanks and reservoirs. -Concrete earth-retaining foundation walls to both the positive and negative side. -Internal concrete surfaces of walls and rafts or slabs to earth-retained structures such as habitable basements, car parks, plant rooms and lift-pits. -Concrete temporary lay down and working areas.
BIOLOGICAL RESISTANCE
DWI regulation 31 approved
THERMAL COMPATIBILITY
>2 MPa
WATER RESISTANCE – POSITIVE & NEGATIVE
10 Bar
SPECIALIST TOOLS REQUIRED
-Spiked roller to ensure captured air is removed and to improve the surface finish -Spiked shoes to allow traverse without damage to the product and to improve the surface finish
DETAIL
Cementitious waterproofing membrane with high adhesion that can be applied very quickly by airless spray. For reservoirs, water tanks, below ground structures, podium decks, balconies and parking areas. Capable of resisting extremely high positive and negative water pressure, HydroCoat 103 2K forms a hard, highly alkaline coating with a degree of elasticity which has greatly enhanced chemical resistance and so is particularly suited for the protection of concrete within sulphate contaminated ground.
It has excellent resistance to the ingress of acid gases, moisture and chlorides to enhance the durability of reinforced concrete and protect highway and coastal structures from chloride attack. HydroCoat 103 2K is reinforced over static joints and at details and changes of direction with HydroCoat 912-RT.
KEY BENEFITS
- Non-toxic when cured.
- Very low VOC content.
- Sprayable – Up to 2 m2 per minute is possible.
- Hard, durable and UV-stable trafficable finish.
- All year round application to damp substrate.
- Can be applied at temperatures as low as 5°C.
- Quick application in one coat to horizontal surfaces.
- Thixotropic – can be applied at 1 mm to vertical surfaces.
- Excellent adhesion to sound prepared concrete substrates and steel.
- Very waterproof – Resistant to 10 bar positive and negative pressure.
- Very high diffusion resistance to carbon dioxide gas and chloride ions; equivalent to 100 mm of concrete cover.
- High build coating of 2 mm eliminates the incidence of small defects seen within thinner membranes.