Newton Waterproofing Hydrocoat 203-rm Cement
HYDROCOAT 203-RM CEMENT
HYDROCOAT 203-RM CEMENT
Rapid Set & High Strength Repair Mortar
Newton HydroCoat 203-RM is a single-component, fast-setting, Portland cement-based structural mortar, used primarily for the durable repair of concrete.
Setting in just 10 minutes at 20ºC, HydroCoat 203-RM is ideal for areas that cannot be taken out of service for long periods, or where the concrete is subjected to heavy wear such as roads, runways, bridges, decks, floors and footpaths.
Polymer-modified, and fibre-reinforced, HydroCoat 203-RM is physically and chemically compatible with the host concrete, quickly exhibiting high adhesive and compressive strength. As a single component, requiring only the addition of water, the resulting mortar is rapid curing with enhanced polymeric properties and reliable strength development which is not significantly affected by low temperature use.
The mortar can be used as supplied up to 100 mm deep, or bulked out with clean, washed, sharp sand to form a high performance screed or for floor or deck repairs up to maximum depth of 300 mm.
INFORMATION
SWIFT STRUCTURAL REPAIR
HydroCoat 203-RM, a single-component, fast-setting Portland cement-based mortar, excels in durable concrete repair. Ideal for roads, runways, bridges, and more, it’s polymer-modified and fibre-reinforced, quickly developing high adhesive and compressive strength.
BRAND
Newton Waterproofing
FORM – ONE COMPONENT
Powder
PRODUCT TYPE
Cement
YIELD PER KG
0.53 Litres
COLOUR
Grey
PACK SIZE
25 kg
DENSITY/SPECIFIC GRAVITY
2.15
ADAPTABLE STRENGTH, RAPID CURE
Physically and chemically compatible with host concrete, HydroCoat 203-RM ensures fast-curing and reliable strength development. As a single component requiring only water, it’s effective up to 100mm deep. For high-performance screeds or deeper repairs (up to 300mm), bulk it with clean, washed, sharp sand.
ADHESIVE BOND – CLASS R4E
> 2 MPa
CHLORIDE ION CONTENT
1.6 MPa
CAPILLARY ABSORPTION
0.108 kg/m-2/h-0.5
CARBONISATION RESISTANCE
Passes
TYPICAL DETAIL
COMPRESSIVE
- Compressive bond – Class R4 : > 45 MPa
- Compressive strength – 1 hour : 14 MPa
- Compressive strength – 2 hours : 20 MPa
- Compressive strength – 4 hour : 30 MPa
- Compressive strength – 1 day : 40 MPa
- Compressive strength – 7 days : 50 MPa
- Compressive strength – 28 days : 60 MPa
ELASTIC MODULUS
26.1 GPa
REACTION TO FIRE
Euroclass A2-s1, d0
THERMAL CAPABILITY – PART 1 – CLASS R4
> 2 MPa
DOWNLOADS
↓ NBS Clause
↓ HydroCoat 203-RM Data Sheet
↓ HydroCoat 203-RM Safety Data Sheet
↓ HydroCoat 203-RM Declaration of Performance
DANGEROUS SUBSTANCES
complies with 5.4
WATER PERMEABILITY COEFFICIENT
2.60x 10-14 m/s
RELIABLE PERFORMANCE IN ALL CONDITIONS
-HydroCoat 203-RM maintains strength even in low temperatures. Its enhanced polymeric properties and rapid cure make it versatile for various applications, ensuring robust and lasting results. -Single-component, fast-setting, Portland cement-based structural mortar, used primarily for the durable repair of concrete. Ideal for roads, runways, bridges, decks, floors and footpaths.
-Polymer-modified, and fibre-reinforced, HydroCoat 203-RM is physically and chemically compatible with the host concrete, quickly exhibiting high adhesive and compressive strength. -As a single component, requiring only the addition of water, the resulting mortar is rapid curing with enhanced polymeric properties and reliable strength development which is not significantly affected by low temperature use. The mortar can be used as supplied up to 100mm deep, or bulked out with clean, washed, sharp sand to form a high-performance screed or for floor or deck repairs up to a maximum depth of 300mm.
KEY BENEFITS
- Dense matrix resists 10 bar water pressure.
- High bond strength exceeds tensile strength of concrete.
- Very high diffusion resistance to acid gases and chloride ions.
- Sets in 10 minutes at 20°C yielding a durable, high strength mortar.
- Economic mortar requiring no substrate or inter-layer priming. Part bags can be mixed.
- Incorporates the latest cement chemistry, fibre and styrene acrylic copolymer technology.
- Reliable strength development, even at sub-zero temperatures, gives rapid return to service.
- Prepackaged material only requires mixing with clean water. Can be bulked out with sand or aggregate.
- Non-toxic when cured and is listed as authorised under Regulation 31 for use in the supply of potable drinking water
- Sulphate resistance to class DS-5/5m of BRE Special Digest 1 and ideally suited for sewage and wastewater applications.