Ruregold Mx-rw High Performanc Plaster
MX-RW HIGH PERFORMANC PLASTER
MX-RW HIGH PERFORMANC PLASTER
High performance mortar for the structural restoration of masonry
MX-RW High Performance is a premixed mortar based on a high pozzolan hydraulic binder and low salt content, select aggregates, additives, and polypropylene fibers. Its particular composition excludes the possibility of chemical reactions with salts (sulphates, carbonates, nitrates, chlorides, etc.) present in the walls of old buildings.
A thixotropic mortar is obtained by adding water. It is ready to use: just add water to obtain a thixotropic mixture with no bleeding or segregation phenomena. It can be applied by trowel or spray.
In cases where a high aesthetic quality of the surface is required, use a suitable finishing coat. The mix is highly adhesive to masonry, tuff, and stone, durable, and suitable for repairs and structural plasters without shrinkage.
INFORMATION
BRAND
Ruregold
PRODUCT TYPPE
Plaster
CONSISTENCY
Consistency Of The Mortar (En 1015-3) : 170 +/- 10 mm
WATER PER
Water Per 100 Kg Of Dry Premix Mortar : 15-16 Liters
FEATURES
- Reaction To Fire (En 13501-1) : Euroclass A1
- Adhesive strength (EN 1015-12) : >= 0,6 N/mm2 - FP: C
- Thermal conductivity/Density (EN 1745-5.4.6) : 0,82 W/mK (as per table)
K++ (CEN/TC 125)
< 350 ppm
MG- ++ (CEN/TC 125)
< 350 ppm
CHARACTERISTICS
- Wet supports
- Ecological
- Easy to install
- Compatible with Masonry
CA++ (CEN/TC 125)
< 350 ppm
NA++ (CEN/TC 125)
< 350 ppm
SPECIFIC WEIGHT
Specific Weight Of Fresh Mortar (En 1015-6) : About 55 Liters
POROSITY
Porosity of the mortar (normal 4/80) - pore volume with d <0.5 : 68 %
COMPLIES WITH EN 998-2
MX-RW High Performances complies with EN 998-2 Mortar for general purposes for external use in elements subject to building code requirements (G).
PACKAGE
25 kg bags on 1,000 kg pallets
SOLUBLE CHLORIDES
< 10 ppm (CEN/TC 125)
COMPRESSION RESISTANCE AT 3, 7, 28 DAYS (EN 1015-11)
>=26>=334>=49,5MPA
BENDING RESISTANCE
Bending resistance at 3, 7, 28 days (en 1015-11) : >=3,1>=3,8>=5,5MPa
CONSUMPTION OF DRY PREMIXED MORTAR
About 18 Kg/m2/cm
ELASTIC MODULUS
Elastic modulus at 28 days (en 13412) : >=15GPa
OPEN POROSITY
Porosity of the mortar (normal 4/80) - open porosity : 23 %
MX-RW HIGH PERFORMANCE
Fiber-reinforced thixotropic mortar for the restoration of masonry, the construction of structural plasters and the preparation of the substrate for the application of structural reinforcements.
DOWNLOADS
↓ Data Sheet
↓ Safety Data Sheet
WORKABILITY
Fresh mortar workability time (20°c) : About 60 min
WATER VAPOR
Water vapor permeability (en 1745-5.4.4) : μ15/35 as par table
SOLUBLE NITRITES/NITRATES (CEN/TC 125)
< 10 ppm
WATER ABSORPTION (EN 1015-18)
0,2((kg/(m2xmin0,5))
PROPERTIES OF THE SYSTEM
-High mechanical resistance to compression and bending. -Excellent adherence to masonry. -High breathability. -Complete compatibility with historical masonry. -Absence of shrinkage cracking. -No bleeding. -High impermeability to water and aggressive aqueous solutions. -High resistance to chemical agents (chlorides, sulphates, acid rain, carbon dioxide, etc.). -Resistance to freezing and thawing cycles. -Ease and speed of installation and finishing.
FIELDS OF APPLICATION
-Repair of damaged masonry structures. -Structural plasters reinforced with glass or steel fibers for the reinforcing of infill walls. -Reinforcement load bearing outer layers reinforced with glass or steel fibers to consolidate vaults. -Preparation layer on masonry elements (brick, tuff, stone) for the application of structural reinforcements with composite materials. -Reconstruction of masonry with the “like for like” replacement technique. -Consolidation of existing walls by restoring the sealing of joints (whether reinforced or not).