Novamix Planofinish Epoxy
PLANOFINISH EPOXY
PLANOFINISH EPOXY
Two component epoxy varnish free of solvents
Glossy, water-based epoxy varnish for the protection of microcement coatings. It is suitable for floors, walls and surfaces of heavy use such as kitchen countertops, bars, tables. It is applied in two coats crosswise undiluted by means of a roller. Also suitable as a pre-treatment in one layer before applying two layers of Planofinish Pu 2kw Mat, On surfaces of heavy use. For indoor use only.
INFORMATION
PALLET
324 L
FORM
liquid
CONSUMPTION
100-150 ml/m² for application in 2 coats
POT LIFE
30 – 60 min. -> 30°C & 60 – 90 min. -> 25°C & ≈2 h -> 15°C
COLOR
Transparent
APPLICATION TEMPERATURE
from +15°C up to +30°C
PACKAGE
Containers (2+1) L
WALKABILITY
4 h > 25°C & ≈10 h > 12°C
USES
Planofinish Epoxy Can Be Used To Protect And Enhance Surfaces Such As:
-Planocolor Premiummicrocement coatings, in interior walls and floors with heavy use, in houses, hotels, restaurants, shops, parking areas, indoor benches and built-in furniture -Natural stones, Skapifran stones -Industrial floors made of concrete treated with surface hardener such as Novadur S By means of power float, in industries, parking areas, gas stations, ramps -Non-absorbent surfaces such as galvanized metal sheet, polyester -Microcement coatings combined with the aliphatic polyurethane varnish – sealer Planofinish Pu 2kw Mat
APPLICATION PROCEDURE
SUBSTRATE PREPARATION
PLANOFINISH EPOXY should be applied on a clean, dry and free from dust surface. The substrate must be insulated from rising moisture. The surface moisture content must not exceed 4%. The application temperature should be between +15°C and +30°C.
PREPARATION OF THE MIXTURE
Components A and B are packaged in containers with a predetermined mixing ratio. Component B is completely added to Component A. Mixing of the two components is done for about 2-3 minutes with an electric mixer at low speed (300 rpm). It is important to stir both the walls and the bottom of the container so that the catalyst is evenly distributed. Allow the mixture to mature for a few minutes and proceed with the application keeping the material workability times.
APPLICATION
Apply at least 2 consecutive layers of the mixture using a suitable roller for varnish. After the first layer turns from milky to transparent, it’s ready to accept the second layer. In any case, take care to penetrate the surface well. The waiting time between the layers is about 60-90 minutes at an ambient temperature of +23°C and the relative humidity less than 80%.
MAINTENANCE
Daily Cleaning Of Surfaces Coated With Planofinish Epoxy Is Done With Neutral Detergents Such As Neutrocleaner Insoluble Or, Dissolved In Water Depending On The Application. For Special Cleaning Cases Such As Rubbers, Shoe Marks, Household Stains, Candles, Etc. It Is Recommended To Use Alcaline Cleaner Dissolved In Water At A Ratio Of 1 ÷ 10 To 1 ÷ 20. If Salt Removal Is Required, Apply Hard Remover Dissolved In Water At A Ratio Of 1 ÷ 3 Or 1 ÷ 4 And Rinse Thoroughly With Water. For More Information, Refer To The Relevant Product Data Sheet.
PRODUCT IDENTITY
| - | COMPONENT A | COMPONENT B |
|---|---|---|
| Form | Liquid | Liquid |
| Color | White | Yellow |
| Chemical base | Epoxy resin | Catalyst |
| Density | 1,05 kg/L | 1,10 kg/L |
| Storage | 12 months in the original package in a dry place | - |
APPLICATION DATA (+23ΟC % & 50% R.H.)
MIXING RATIO
Part Α : Part :Β ≈ 2 : 1
RE COATING
After 30 - 60 min. in 230C
DENSITY OF THE MIX
1,05 ± 0,05 kg/L
COMPLETE POLYMERIZATION
After 7 days in 230C
RESISTANCE TO TEMPERATURE CHANGE
from -300C to +800C
ABRASION RESISTANCE
50 mg Tabertest ASTM D 4060 (CS 10/1000/1000)
FLEXIBILITY (TORSION TEST)
Successful (ASTM D522), 1800 bend, 1/8"m
GLOSS IN 600
85
APPLICATION TEMPERATURE
from +15°C to +30°C